Lithium iodate
Lityum yodat
I-O bog'lanish uzunligi bilan lityum yodatning skelet formulasi
Lityum yodatning kristalli tuzilishi, yodlar birlik hujayrasida joylashgan
Ismlar
IUPAC nomi
Lityum yodat
Identifikatorlar
3D model (JSmol)
ChemSpider
ECHA ma'lumot kartasi100.033.954 Buni Vikidatada tahrirlash
EC raqami
  • 237-365-2
UNII
BMT raqami1479
Xususiyatlari
LiIO3
Tashqi ko'rinishOq gigroskopik kristallar
HidiHidi yo'q
Zichlik4.487 g / sm3[1]
Erish nuqtasi 420-450 ° C (788-842 ° F; 693-723 K)[1][3][5]
Suvsiz:
89,4 g / 100 ml (10 ° C)
82,7 g / 100 ml (25 ° C)
78,4 g / 100 ml (40,1 ° C)
73 g / 100 ml (75,6 ° C)[1]
Gemihidrat:
80,2 g / 100 ml (18 ° C)[2]
EriydiganlikErimaydi EtOH[3]
−47.0·10−6 sm3/ mol
Issiqlik o'tkazuvchanligi1,27 Vt / m · K (a o'qi)
0,65 Vt / m · K (c-o'qi)[1]
1.8875 (20 ° C)
1.6 (RT)
nHe-Ne:
1.8815 (20 ° C)[1]
1.5928 (RT)[4]
Tuzilishi
Olti burchakli,[3] hP10[6]
P6322, № 182[6]
622[6]
a = 5.46 (9) Å, v = 5.15 (5) Å[6]
a = 90 °, ph = 90 °, ph = 120 °
Xavf
GHS piktogrammalariGHS03: oksidlovchiGHS07: zararliGHS08: sog'liq uchun xavfli[7]
GHS signal so'ziXavfli
H272, H315, H319, H335, H360[7]
P201, P220, P261, P305 + 351 + 338, P308 + 313[7]
NFPA 704 (olov olmos)
Boshqacha ko'rsatilmagan hollar bundan mustasno, ulardagi materiallar uchun ma'lumotlar berilgan standart holat (25 ° C [77 ° F], 100 kPa da).
tekshirishY tasdiqlang (nima bu tekshirishY☒N ?)
Infobox ma'lumotnomalari

Lityum yodat (LiIO3) manfiy bir tomonlama kristaldir[1] chiziqli bo'lmagan, akusto-optik va piezoelektrik dasturlar uchun. U 347 nm yoqutli lazer uchun ishlatilgan.[9][10]

Xususiyatlari

Mohsning qattiqligi lityum yodatning 3,5-4. Uning chiziqli issiqlik kengayishi 298 K (25 ° C; 77 ° F) da koeffitsient 2.8 · 10 ga teng−5/ ° C (a o'qi) va 4.8 · 10−5/ ° C (c-o'qi).[1] Uning g-shaklga o'tishi 50 ° C (122 ° F) da boshlanadi va bu qaytarib bo'lmaydigan.[5]

Adabiyotlar

  1. ^ a b v d e f g "Kamdan kam ishlatiladigan va arxivlangan kristallar". Lineer bo'lmagan optik kristallar: to'liq tadqiq. 2005. 364-368 betlar. doi:10.1007/0-387-27151-1_8. ISBN 978-0-387-27151-4 https://web.archive.org/web/20140808232709/http://www.webcryst.com/zh/download/finish/6-/477-liio3-lithium-iodate.html. Arxivlandi asl nusxasi 2014-08-08 da. Olingan 2014-08-08. Yo'qolgan yoki bo'sh sarlavha = (Yordam bering)
  2. ^ Seidell, Atherton; Linke, Uilyam F. (1919). Anorganik va organik birikmalarning eruvchanligi (2-nashr). Nyu-York shahri: D. Van Nostrand kompaniyasi. p.374.
  3. ^ a b v Lide, Devid R., ed. (2009). CRC Kimyo va fizika bo'yicha qo'llanma (90-nashr). Boka-Raton, Florida: CRC Press. ISBN 978-1-4200-9084-0.
  4. ^ Polyanskiy, Mixail. "LiIO3 (Lityum yodat) ning sinishi ko'rsatkichi - Herbst-o". http://www.refractiveindex.info. Olingan 2014-08-08. Tashqi havola | veb-sayt = (Yordam bering)
  5. ^ a b Taysier, Jeremie; Dantek, Ronan Le; Galez, Kristin; Mugnier, Yannik; Bulot, Jak; Plenet, Jan-Klod (2003-11-20). Endryus, Devid L; Gaburro, Zeno; Kartrayt, Aleksandr N; Li, Charlz Y. (tahrir). "LiIO3 SiO tarkibidagi nanokristallar2 xerogels, chiziqli bo'lmagan optika uchun yangi material ". SPIE ishi. Nanokristallar va organik va gibrid nanomateriallar. 5222 (26): 26. CiteSeerX 10.1.1.605.1743. doi:10.1117/12.507309. S2CID 136547473.
  6. ^ a b v d Zakariasen, VX; Olof, F.A.BartaLars (1931-06-15). "Lityum yodatning kristalli tuzilishi". Jismoniy tekshiruv xatlari. 37 (12): 1626–1630. doi:10.1103 / PhysRev.37.1626.
  7. ^ a b v Sigma-Aldrich Co., Lityum yodat. 2014-08-08 da qabul qilingan.
  8. ^ "Suvsiz lityum yodat SDS" (PDF). https://www.pfaltzandbauer.com. Konnektikut, AQSh: Pfaltz & Bauer, Inc. Arxivlangan asl nusxasi (PDF) 2014-08-10. Olingan 2014-08-08. Tashqi havola | veb-sayt = (Yordam bering)
  9. ^ Xavf, W. P.; Gosnell, T. R .; Nurmikko, A. V. (9 yanvar 2003). Yilni ko'k-yashil lazerlar. Kembrij universiteti matbuoti. p. 123. ISBN 978-0-521-52103-1. Olingan 13 dekabr 2012.
  10. ^ Nikogosyan, Devid N. (2005 yil 4-yanvar). Lineer bo'lmagan optik kristallar: to'liq tadqiq. Springer. p. 371. ISBN 978-0-387-22022-2. Olingan 13 dekabr 2012.